OS1204 放射光CTによるアルミニウム鋳造合金の低サイクル疲労破壊挙動評価

• 松村 圭悟

  福井大学大学院工学研究科

• アギアルデソウザ ヴィニシウス

  東北大学大学院工学研究科

• 桑水流 理

  福井大学大学院工学研究科

• 小林 正和

  豊橋技術科学大学

• 戸田 裕之

  九州大学大学院工学研究院

書誌事項

タイトル別名

• OS1204 Fracture Behavior Evaluation of Cast Aluminum Alloy under Low Cycle Fatigue using Synchrotron Radiation CT

抄録

The crack initiation mechanism of cast aluminum alloy was addressed to quantitatively evaluate the fatigue strength. The synchrotron radiation microtomography was employed to visualize the three-dimensional damage around pores and Si particles. Two types of specimens were prepared for the low cycle fatigue test. The temperature of solution treatment was different, and it yields a difference in the shape of Si particles. After a certain cycles of fatigue, a catastrophic damage around many Si particles happened and they connected to each other so as to form a crack. The scanning electron microscopy after the test showed that the type of damage was the break of long Si particles or the interface debonding around round Si particles.

収録刊行物

• M&M材料力学カンファレンス

  M&M材料力学カンファレンス 2014 (0), _OS1204-1_-_OS1204-3_, 2014

  一般社団法人 日本機械学会

キーワード

• Low Cycle Fatigue
• Aluminum Alloy
• Crack Initiation
• Polycrystalline Structure
• in situ Observation
• Synchrotron Radiation
• Microtomography
• 4D Imaging

詳細情報

• CRID: 1390001205875560832
• NII論文ID: 110009939621
• DOI: 10.1299/jsmemm.2014._os1204-1_
• ISSN: 24242845
• Web Site: https://www.jstage.jst.go.jp/article/jsmemm/2014/0/2014__OS1204-1_/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可