- OS1605 Ferroelastic Properties of Cathode Materials of Solid Oxide Fuel Cells
抄録
Temperature and frequency dependence of Young's modulus and internal friction of La_<0.6>Sr_<0.4>Co_<0.2>Fe_<0.8>O_<3-δ> were evaluated by dynamic mechanical analysis. A relaxation peak in the internal friction which follows a significant decrease in the Young's modulus was observed. It was suggested that the peak was derived from domain reorientations. An introduction of oxygen vacancies into the sample significantly changed the temperature dependence of the Young's modulus and the internal friction. The Young's modulus became larger especially below 400 K. A small peak which depended on the oxygen vacancy concentration was observed when the oxygen vacancies were introduced. This peak was considered to be due to oxygen vacancy diffusion. Such significant changes in the temperature dependence of the Young's modulus and the internal friction may be caused by crystal structure change and pinning of domain walls by the oxygen vacancies.
収録刊行物
-
- M&M材料力学カンファレンス
-
M&M材料力学カンファレンス 2014 (0), _OS1605-1_-_OS1605-3_, 2014
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205875478400
-
- NII論文ID
- 110009939662
-
- ISSN
- 24242845
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可