- OS2109 Influence of grain size for slip band formation in carbon steel film under cyclic shear loading
抄録
A metal thin film doesn't necessarily appear general fatigue behavior like a bulk material. By a balk and film material, there is difference of restricted state because of differing in the number of grains to the direction of film thickness. In this research the diagram of ratio of slipped grains and number of cycle was sorted by film thickness/grain size ratio in carbon steel thin film under cyclic shear loading. Then slip ratio under film thickness/grain size ratio 0.80 saturated. The influence of grain size was considered to slip band formation by examining grain's existence frequency to direction of film thickness. It was bringing close to actual grains by extending two dimensions grain size to three dimensions. As a result, there was the relation between the slip ratio and the grain's cumulate existence frequency in the value whose film thickness/grain size ratio are near 0.9.
収録刊行物
-
- M&M材料力学カンファレンス
-
M&M材料力学カンファレンス 2014 (0), _OS2109-1_-_OS2109-3_, 2014
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680851766528
-
- NII論文ID
- 110009939738
-
- ISSN
- 24242845
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可