J0320402 金属レーザ積層造形法による発泡アルミニウム表面への緻密層形成([J032-04]ポリマー・セラミックス・メタル多孔質材料の開発と応用(4),材料力学部門) [in Japanese] J0320402 Fabrication of Nonporous Layer on Surface of Aluminum Foam by Selective Laser Melting [in Japanese]
Access this Article
Surface pores of a closed-cell type aluminum foam were filled with aluminum powder by selective laser melting (SLM). The relationship between the laser irradiation conditions and solidification characteristics of aluminum powder was investigated with one-line laser irradiation. The aluminum powder was continuously melted and solidified with a laser spot diameter of 0.6 mm and a scanning speed of 10-20 mm/s. According to the successful melting and solidification conditions, SLM was applied to the surface pores of a closed-cell type aluminum foam supplied with aluminum powder. The supplied aluminum powder was melted and welded to the aluminum foam. As the result, the aluminum foam with nonporous surface layer (sandwich structure) was successfully fabricated.
- The Proceedings of Mechanical Engineering Congress, Japan
The Proceedings of Mechanical Engineering Congress, Japan 2014(0), _J0320402--_J0320402-, 2014
The Japan Society of Mechanical Engineers