20414 AFMを用いたCu/Moナノ積層コーティングの凝着特性調査  [in Japanese] 20414 Study on adhesion properties of Cu/Mo nano-laminated coatings by AFM  [in Japanese]

Access this Article

Author(s)

Abstract

Nano-laminated coatings have good tribological properties. But, the friction reduction mechanism is not sufficiently investigated yet. This report aimed to investigate the mechanism from adhesion properties. Two kind of Cu/Mo Nano-laminated coatings, Cu single coating and Mo single coating were formed by sputtering. Sliding test was performed for each specimen. Cu/Mo nano-laminated coating showed the best tribological properties. After sliding test, Cu/Mo nano-laminated coating was analyzed by Atomic Force Microscop (AFM). Cu/Mo nano-laminated coating had mixed surface of Cu and Mo. In order to investigate adhesion properties, friction coefficient of the mixed surface was measured by Friction Curve with different frequency. From the results, it was shown that the mixed surface had inhibitory effect of friction increase. It suggested that the mixed surface had adhesion inhibitory effect and friction reduction effect of Cu/Mo nano-laminated coatings was caused by the adhesion inhibitory effect.

Journal

  • The Proceedings of Conference of Kanto Branch

    The Proceedings of Conference of Kanto Branch 2014.20(0), _20414-1_-_20414-2_, 2014

    The Japan Society of Mechanical Engineers

Codes

Page Top