CRYSTAL GROWTH OF A HECTORITE-LIKE LAYERED SILICATE ON MONODISPERSE SPHERICAL SILICA PARTICLES WITH DIFFERENT DIAMETERS
-
- OKADA TOMOHIKO
- Department of Chemistry and Material Engineering, Faculty of Engineering, Shinshu University
-
- SUZUKI ASUKA
- Department of Chemistry and Material Engineering, Faculty of Engineering, Shinshu University
この論文をさがす
抄録
Fine crystals of hectorite-like layered silicate formed using hydrothermal reactions on monodisperse spherical silica particles with diameters of 0.2, 0.6 and 1.0 μm. The reactions were performed in a colloidal spherical silica suspension with lithium and magnesium ions under alkaline conditions at 373 K in a rotating Teflon-lined autoclave at the LiF:MgCl_2:SiO_2 molar ratio of 0.21:0.8:8.0. The grain size distributions were quite uniform irrespective of the silica size in the initial mixtures, as a result of the high rate of heterogeneous nucleation reaction than that of the homogeneous nucleation. The amount of a cationic surfactant that was intercalated tended to be large when the grain size of the silica spheres was small, while the negative layer charge of the hectorite-like silicate was same extent.
収録刊行物
-
- Clay Science
-
Clay Science 19 (2), 45-51, 2015
一般社団法人 日本粘土学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204113338752
-
- NII論文ID
- 110009985138
-
- NII書誌ID
- AA00607148
-
- ISSN
- 21863555
- 00098574
-
- HANDLE
- 10091/00020339
-
- NDL書誌ID
- 026739129
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可