P-21 ガラス系複合材料に対する表面処理効果(接着,一般講演(ポスター発表),第66回日本歯科理工学会学術講演会)
書誌事項
- タイトル別名
-
- P-21 Surface treatment effects for a glass-based composite material
この論文をさがす
抄録
Sandblasting with 50 μm at 0.1-0.4MPa was performed to a glass-based composite material (Enamic, Kayo), and then topographical and morphological change was evaluated. Shear bond strengths on the Enamic were measured with six kinds of resin-based cements after storing 24 hours in water and suffering thermal cycle for 10^4 cycles. Surface roughness and surface waviness were increased with the increases of treatment pressure; however glass filler fractured with pressure over 0.3MPa. We seemed shear bond strength of Enamic was suitable (except with MCE) enough to be applied to the CAD/CAM crown.
収録刊行物
-
- 日本歯科理工学会誌
-
日本歯科理工学会誌 34 (5), 347-, 2015-09-15
一般社団法人日本歯科理工学会