Microscopic Surface Change of Polycrystalline Aluminum duringTensile Plastic Deformation
この論文をさがす
抄録
Roughening on free surface of polycrystalline metal during plastic deformation is closely related to the inhomogeneous deformation in the respective grain at the surface. Uniaxial tensile tests are carried out on annealed pure aluminum sheet specimens with various averaged grain sizes. The roughening is measured by a 3-dimensional stylus instrument to examine the roughness change in both sides of specimen surfaces at each strain. The irregularities on one side are reversed on the backside, when the averaged grain size is as large as the thickness of the specimen. Discussions are made on the relation between the surface shapes of both sides adopting the cross correlation factor. The strains of respective grains are also measured from the grain boundary shape before and after plastic deformation. There are some deviations in the strains of the grains and their standard deviation increases with the applied strain.
収録刊行物
-
- Memoirs of the Faculty of Engineering, Okayama University
-
Memoirs of the Faculty of Engineering, Okayama University 39 (1), 7-15, 2005-01
Faculty of Engineering, Okayama University
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390572174534507776
-
- NII論文ID
- 120002308149
-
- NII書誌ID
- AA10699856
-
- ISSN
- 04750071
-
- DOI
- 10.18926/14135
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- IRDB
- CiNii Articles