Fabrication of Anodic Porous Alumina via Acetylenedicarboxylic Acid Anodizing
書誌事項
- タイトル別名
-
- Fabrication of Anodic Nanoporous Alumina via Acetylenedicarboxylic Acid Anodizing
抄録
The nano-morphologies of anodic porous alumina formed via anodizing in a new electrolyte, acetylenedicarboxylic acid (ADCA), are described. Anodic oxides grew uniformly on the aluminum at voltage of 87.5-95.0 V, but a burned black oxide film was formed at higher voltage. The burning voltage and the current density under steady-state oxide growth decreased with solution temperature. An anodic porous alumina film with a cell size of 250 nm and nanopores measuring 100 nm could be successfully obtained by ADCA anodizing. The anodic porous alumina possessed numerous non-straight nanopores due to the branching and extinction of the nanopores during anodizing.
収録刊行物
-
- ECS Electrochemistry Letters
-
ECS Electrochemistry Letters 3 (7), C25-C28, 2014
The Electrochemical Society
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1050001339016784000
-
- NII論文ID
- 120005446633
-
- ISSN
- 21628734
- 21628726
-
- HANDLE
- 2115/56407
-
- 本文言語コード
- en
-
- 資料種別
- journal article
-
- データソース種別
-
- IRDB
- Crossref
- CiNii Articles
- KAKEN