Evolution of long-period stacking ordered structures on annealing as-cast Mg85Y9Zn6 alloy ingot observed by synchrotron radiation small-angle scattering

Access this Article

Search this Article

Abstract

The nanostructure of Mg(85)Y(9)Zn(6) ternary alloy ingot with long-period stacking ordered structure has been examined by synchrotron radiation small-angle X-ray scattering. The scattering patterns showed sharp reflections corresponding to large domains of 10H, 18R and 14H structures, with in-plane ordering. After annealing at 673 K, the peak intensity of 18R increased, and the diffraction peak corresponding to in-plane ordering sharpened. The domain size of in-plane ordering was much smaller than the domain thickness of 18R in the stacking direction.

Journal

  • Scripta Materialia

    Scripta Materialia 68(8), 575-578, 2013-04

    Elsevier Ltd.

Codes

  • NII Article ID (NAID)
    120005593593
  • NII NACSIS-CAT ID (NCID)
    AA11067905
  • Text Lang
    ENG
  • Article Type
    journal article
  • ISSN
    1359-6462
  • Data Source
    IR 
Page Top