Nanowire of hexagonal gallium oxynitride: Direct observation of its stacking disorder and its long nanowire growth

• Masubuchi, Yuji

• Yamaoka, Ryohei

• Tohei, Tetsuya

• Mizoguchi, Teruyasu

• Ikuhara, Yuichi

• Kikkawa, Shinichi

Abstract

The crystal structure of gallium oxynitride nanowire was investigated by using scanning transmission electron microscopy. Gallium oxynitride nanowire was directly observed to have a biphasic wurtzite and zinc-blende structure. There was a stacking disorder of several atomic layers between the two phases. The new biphasic nanowire formed due to the presence of Ni in starting material because its nitride has a zinc-blende structure whereas gallium oxynitride has the wurtzite structure. Crystal growth of gallium oxynitride nanowires was studied using seed crystals. Seed crystals and amorphous gallium oxide precursors were annealed under different ammonia flow rates to grow gallium oxynitride nanowires. The nanowires grew to length of 150 μm but they did not grow laterally when the ammonia flow rate was 50 mL/min.

Journal

• Journal of the European Ceramic Society

  Journal of the European Ceramic Society 32 (9), 1989-1993, 2012-07

  Elsevier

Keywords

• Fibres
• Electron microscopy
• Oxynitrides
• Defects

Details

• CRID: 1050282813987488896
• NII Article ID: 120005946650
• HANDLE: 2115/49511
• ISSN: 09552219
• Text Lang: en
• Article Type: journal article
• Data Source:
  • IRDB
  • CiNii Articles