Magnetocaloric effect, thermal conductivity, and magnetostriction of epoxy-bonded La(Fe0.88Si0.12)13 hydrides

DOI DOI 機関リポジトリ Web Site Web Site 参考文献6件

書誌事項

タイトル別名
  • Magnetocaloric effect, thermal conductivity, and magnetostriction of epoxy-bonded La(Fe<sub>0.88</sub>Si<sub>0.12</sub>)<sub>13</sub> hydrides

抄録

金沢大学理工研究域数物科学系

Magnetic materials with large magnetocaloric effect are significantly important for magnetic refrigeration. La(Fe0.88Si0.12)13 compounds are one of the promising magnetocaloric materials that have a first order magnetic phase transition. Transition temperature of hydrogenated La(Fe0.88Si0.12)13 increased up to room temperature region while keeping metamagnetic transition properties. From view point of practical usage, bonded composite are very attractive and their properties are important. We made epoxy bonded La(Fe0.88Si0.12)13 hydrides. Magnetocaloric effect was studied by measuring specific heat, magnetization, and temperature change in adiabatic demagnetization. The composite had about 20% smaller entropy change from the hydrogenated La(Fe0.88Si0.12)13 powder in 2 T. Thermal conductivity of the composite was several times smaller than La(Fe,Si)13. The small thermal conductivity was explained due to the small thermal conductivity of epoxy. Thermal conductivity was observed to be insensitive to magnetic field in 2 T. Thermal expansion and magnetostriction of the composite material were measured. The composite expanded about 0.25% when it entered into ferromagnetic phase. Magnetostriction of the composite in ferromagnetic phase was about 0.2% in 5 T and much larger than that in paramagnetic phase. The composite didn't break after about 100 times magnetic field changes in adiabatic demagnetization experiment even though it has magnetostriction. © Published under licence by IOP Publishing Ltd.

収録刊行物

参考文献 (6)*注記

もっと見る

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ