フッ素添加水溶液で電解処理したSUS304ステンレス鋼の耐食性および不動態皮膜の解析  [in Japanese] Corrosion resistance of SUS304 stainless steel after electrolytic treatment with aqueous solution containing fluorine and the analysis of passive film  [in Japanese]

Access this Article

Search this Article

Abstract

The corrosion resistance of SUS304 stainless steel before and after electrolytic treatment with aqueous solutions containing fluorine was investigated and the FE-TEM, XPS and TOF-SIMS analyses were conducted to the passive film. The corrosion resistance of the steel in acidic 6.0% FeCl3 solution was enhanced to more than twice by the electrolytic treatment, and the pitting potential of 2B surface in 1.0 M NaCl solution increased from 283 mV to 363 mV (vs. SSE). The enhancement is likely related to the formation of a stable, dense and uniform passive film, which should be attributed to the enrichment of chromium and the formation of stable chromium fluoride in the passive film, the removal of impurities and inclusions, and the suppression of specific adsorption of chloride ions due to the electronegative repulsion of fluoride.

Journal

  • 広島工業大学紀要. 研究編

    広島工業大学紀要. 研究編 53, 229-238, 2019-02

    広島工業大学

Codes

  • NII Article ID (NAID)
    120006560035
  • NII NACSIS-CAT ID (NCID)
    AA11599110
  • Text Lang
    JPN
  • Article Type
    departmental bulletin paper
  • Journal Type
    大学紀要
  • ISSN
    1346-9975
  • NDL Article ID
    029507246
  • NDL Call No.
    Z14-307
  • Data Source
    NDL  IR 
Page Top