Application of Layered Nickel Double Hydroxide for Alkali Secondary Battery Using the Liquid Phase Deposition Method
Abstract
The effects of fluoride ions scavenger in the liquid phase deposition synthesis of nickel-aluminum layered double hydroxide/carbon (Ni-Al LDH/C) composite have been investigated. Al(NO3)3.9H2O, AlCl3, Al metal plate, and a mixed solution of [Al(NO3)3.9H2O and H3BO3] were employed as F- scavengers. In the case that Al material is solely used as F- scavenger, α-nickel hydroxide is the predominant phase, and a small amount of β-phase is detected. In contrast pure phase Ni-Al LDH/C composites, isostructural and isomorphic to α-Ni(OH)2 are obtained when a mixed solution of Al(NO3)3.9H2O and H3BO3 is used at any range of Al content. High purity LDHs without cationic species exhibited good stability in 6M KOH for 7 days. Short-term charge-discharge measurements at 1C-rate for the electrodes containing 0, 13.6 and 17.8 Al mol % showed an increase of the discharge capacity with increasing Al content.
Journal
-
- ECS Transactions
-
ECS Transactions 19 (27), 41-46, 2009
Electrochemical Society
- Tweet
Details 詳細情報について
-
- CRID
- 1050012570392973696
-
- NII Article ID
- 120006629940
-
- ISSN
- 19386737
- 19385862
-
- HANDLE
- 20.500.14094/90005894
-
- Text Lang
- en
-
- Article Type
- journal article
-
- Data Source
-
- IRDB
- CiNii Articles
- KAKEN