Red-emission over a wide range of wavelengths at various temperatures from tetragonal BaCN<sub>2</sub>:Eu<sup>2+</sup>
書誌事項
- タイトル別名
-
- Red-emission over a wide range of wavelengths at various temperatures from tetragonal BaCN2:Eu2+
- Red-emission over a wide range of wavelength at various temperatures from tetragonal BaCN2:Eu2+
抄録
A new polymorph of BaCN2 was obtained via a simple nitridation reaction of BaCO3 under an NH3 flow at 900 1C. The product was analyzed via single crystal X-ray diffraction and infrared spectroscopy, and it was found to have a tetragonal I4/mcm crystal structure (space group no. 140) with a = 0.60249(4) nm and c = 0.71924(5) nm. In this structure, each Ba2+ cation is situated in the square antiprism of N atoms of NCN(2-)anionic groups. Eu2+ doped BaCN2 can be excited by irradiation of blue and green light (from 400 to 550 nm), and it generates an intense red emission peak at 660 nm with a quantum efficiency of 42% in response to 465 nm excitation at room temperature. The peak emission wavelength varies over an extremely wide range of temperature, from 640 nm at 500 K to 680 nm at 80 K, and this red-shift with decreasing temperature is attributed to a unit cell shrinkage that results in significant crystal field splitting of the 5d energy levels of the Eu2+ ions.
収録刊行物
-
- Journal of materials chemistry C
-
Journal of materials chemistry C 6 (24), 6370-6377, 2018-06-28
Royal Society of Chemistry
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1050001202676325760
-
- NII論文ID
- 120006648347
-
- ISSN
- 20507534
- 20507526
-
- HANDLE
- 2115/74809
-
- 本文言語コード
- en
-
- 資料種別
- journal article
-
- データソース種別
-
- IRDB
- Crossref
- CiNii Articles
- KAKEN