Evaluation of Mechanical and Shrinkage Behavior of Cold-weather Cementitious Mortars Mixed with Nitrite-Nitrate Based Accelerator
抄録
Recently, calcium nitrite (Ca(NO2)2) and calcium nitrate (Ca(NO3)2) have been increasingly used as the main components of salt- and alkali-free anti-freezing agents, for promoting concrete hydration in cold-weather concreting. With an increase in the amount of nitrite-based accelerator, the hydration of C3A, C3S, and βC2S in the cement is accelerated, thereby improving its early strength and effectively preventing the initial frost damage. Meanwhile, with an increase in the amount of nitrite-based accelerator, the expansion and shrinkage of the concrete—and, therefore, the crack occurrence—are expected to increase. In this study, various experiments were conducted on shrinkage, crack initiation, and the development of mortar containing a considerable amount of a nitrite-based accelerator. The result confirmed that, as the amount of nitrite-based accelerator was increased, the shrinkage was increased, and cracking in early age was more likely to occur, compared to the cases without the addition of this accelerator.
収録刊行物
-
- MATERIALS
-
MATERIALS 13 (17), 2020
MDPI
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1051412328430723584
-
- NII論文ID
- 120006900336
-
- ISSN
- 19961944
-
- HANDLE
- 10258/00010312
-
- 本文言語コード
- en
-
- 資料種別
- journal article
-
- データソース種別
-
- IRDB
- CiNii Articles