- Low Temperature Synthesis and Thermoelectric Properties of β-FeSi<SUB>2</SUB>
- β-FeSi2の低温合成と焼結体の熱電特性
- ベータ FeSi2 ノ テイオン ゴウセイ ト ショウケツタイ ノ ネツデントクセイ
- Low Temperature Synthesis and Thermoelectric Properties of β-FeSi<SUB>2</SUB>
この論文をさがす
抄録
β-FeSi2 powders were prepared by solid-state reaction between iron and silicon powders. After the reaction, sintered n-type and p-type β-FeSi2 were prepared by hot pressing at 900°C for 1h under 55MPa in Ar. The effects of the amount of KCl and the most suitable reaction temperature on the solid-state reaction were investigated. β-FeSi2 powder was prepared by adding 5.0mass%KCl at 850°C for 5h in Ar. After the reaction, sample crushed by ball milling and KCl was removed by washing with pure water. But in hot pressed samples, small amount of ε-phase appeared. To reduce the ε-phase, excess 3.0mass%Si were added to the β-phase powders before hot pressing. The relative density of the obtained sintered body was about 92%.<BR>Thermoelectric properties of sintered body of β-phase only (Fe0.95M0.05Si2.21, M=Co, Cr) and sintered body including ε-phase (Fe0.95M0.05Si2.1, M=Co, Cr) were evaluated. As a result, power factor (α2/ρ) of sintered body including ε-phase was superiorer to sintered body of β-phase only.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 53 (6), 523-528, 2006
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681284179072
-
- NII論文ID
- 130000057872
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 8025932
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可