Low Cycle and Thermo-Mechanical Fatigue of Friction Welded Dissimilar Superalloys Joint
-
- SAKAGUCHI Motoki
- Department of Mechanical Engineering, Nagaoka University of Technology
-
- SANO Atsushi
- Department of Mechanical Engineering, Nagaoka University of Technology
-
- TRAN Tra Hung
- Department of Mechanical Engineering, Nagaoka University of Technology
-
- OKAZAKI Masakazu
- Department of Mechanical Engineering, Nagaoka University of Technology
-
- SEKIHARA Masaru
- Hitachi Ltd., Material Research Laboratory
抄録
The high temperature strengths of the dissimilar friction welded superalloys joint between the cast polycrystalline Mar-M247 and the forged IN718 alloys have been investigated under low cycle and thermo-mechanical fatigue loadings, in comparison with those of the base metals. The experiments showed that the lives of the dissimilar joints were significantly influenced by the test conditions and loading modes. Not only the lives themselves but also the failure positions and mechanisms were sensitive to the loading mode. The fracture behaviors depending on the loading modes and test conditions were discussed, based on the macroscopic elastic follow-up mechanism and the microstructural inhomogeneity in the friction weld joint.
収録刊行物
-
- JSMME
-
JSMME 2 (12), 1508-1516, 2008
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205265429760
-
- NII論文ID
- 130000079148
-
- ISSN
- 18809871
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可