Hydrogen storage property of nanoporous carbon materials prepared from rice husk
-
- TODA Ikumi
- Nagaoka University of Technology
-
- ONO Hiroki
- Nagaoka University of Technology
-
- TAKAHATA Tomokazu
- Nagaoka University of Technology
-
- OHSHIO Shigeo
- Nagaoka University of Technology
-
- AKASAKA Hiroki
- Nagaoka University of Technology
-
- HIMENO Syuuji
- Nagaoka University of Technology
-
- KOKUBU Toshinori
- Miyakonojo National College of Technology
-
- SAITOH Hidetoshi
- Nagaoka University of Technology
書誌事項
- タイトル別名
-
- Hydrogen Storage Property of Nanoporous Carbon Materials Prepared from Rice Husks
抄録
Nanoporous carbon materials for use as hydrogen storage materials were fabricated from rice husks. Rice husks from agricultural waste changed to porous carbon materials by heat treating and KOH activation. The specific surface area of the porous carbon materials increased from 11 to 2061 m2/g as the KOH weight ratio increased. The pore volume of the materials also increased from 0.01 to 0.88 cm3/g by KOH activation. The pore sizes of the activated porous carbon materials were distributed around 0.6 and 1.2 nm at micro-pore ranges. These results suggested porous carbon material have micro-pore structure. The hydrogen storage capacity of the porous carbon materials showed a 0.62 wt.% at 298 K under 12 MPa. The fabrication of hydrogen storage materials from agricultural waste rice husks was achieved. The results indicate that porous carbon materials synthesized from rice husks have micro-pore structures which influence their hydrogen storage capabilities.
収録刊行物
-
- JSMME
-
JSMME 3 (12), 1306-1311, 2009
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205263927808
-
- NII論文ID
- 130000147520
-
- BIBCODE
- 2009JSMME...3.1306T
-
- ISSN
- 18809871
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可