- SAKAGUCHI Motoki
- Department of Mechanical Engineering, Nagaoka University of Technology
-
- SASAKI Yosuke
- Department of Mechanical Engineering, Nagaoka University of Technology
-
- OKAZAKI Masakazu
- Department of Mechanical Engineering, Nagaoka University of Technology
-
- NAMBA Koichi
- Gas Turbine Power Plant Group, Mitsui Engineering & Shipbuilding CO., LTD
抄録
Local area fatigue crack propagation resistance of a retired gas turbine vane made of a Ni-based superalloy which had been operating for about 20000 h. in a 1100 °C level land-based gas turbine, was experimentally evaluated. Here, special efforts were made to build up a new testing apparatus to assess the fatigue crack propagation resistance, using the miniature size specimens extracted from the vane. The miniature specimens were extracted from the leading and the trailing edges, respectively. It was shown that the fatigue crack grew associating with the rate significantly higher at the trailing than at the leading edge part. It was also indicated that the crack propagation rates in the miniature specimen were generally higher than those in the standard size specimen. Furthermore, it was also shown that an application of a simple reheat treatment was effective to recover the crack propagation resistance for the post service vane.
収録刊行物
-
- JSMME
-
JSMME 4 (2), 131-142, 2010
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205264309504
-
- NII論文ID
- 130000255489
-
- ISSN
- 18809871
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可