Preparation of siloxane-containing vaterite/poly (lactic acid) hybrid fibermats with improved ductility for bone regeneration
-
- LIN Sen
- Department of Frontier Materials, Graduate School of Engineering, Nagoya Institute of Technology
-
- FUJIKURA Kie
- Department of Frontier Materials, Graduate School of Engineering, Nagoya Institute of Technology
-
- OBATA Akiko
- Department of Frontier Materials, Graduate School of Engineering, Nagoya Institute of Technology
-
- KASUGA Toshihiro
- Department of Frontier Materials, Graduate School of Engineering, Nagoya Institute of Technology
この論文をさがす
抄録
Siloxane-containing vaterite (SiV)/poly (L-lactic acid) (PLLA) hybrid (SiPVH) fibermats have superior potential for bone regeneration applications. Present work aims to optimise its performance as bone filler materials by improving its mechanical properties and maintaining its bioactivity. The SiPVH fibermats were prepared with melt-blending and electrospinning protocols and modified by increasing PLLA content from 40 to 70 wt %. The tensile strength of the modified fibermat was 10 times higher than that of the original one. The elongation before failure of the modified fibermat was twice as large as that of the original one. The mechanism of their enhancement was investigated by observing failure points in the fibermats after the tensile tests: necking of fibers, which occurred in the modified fibermats, was believed to contribute to the enhanced mechanical properties. The modified fibermat showed the relatively constant release of ionic silicon-species in Tris-buffer solution and could be coated with hydroxyapatite by soaking in simulated body fluid.
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 118 (1379), 623-625, 2010
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680263033728
-
- NII論文ID
- 130000304602
-
- NII書誌ID
- AA12229489
-
- ISSN
- 13486535
- 18820743
-
- NDL書誌ID
- 10732146
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可