Production of Hollow Spheres of Eutectic Tin-Lead Solder through a Coaxial Nozzle
-
- VU Truong V.
- Graduate School of Science and Engineering, Ritsumeikan University
-
- TAKAKURA Hideyuki
- Graduate School of Science and Engineering, Ritsumeikan University
-
- WELLS John C.
- Graduate School of Science and Engineering, Ritsumeikan University
-
- MINEMOTO Takashi
- Ritsumeikan Global Innovation Research Organization, Ritsumeikan University
抄録
Hollow eutectic tin-lead solder spheres with diameters from 3.5 to 4.5 mm have been produced directly from the melt. Raw solder placed in a crucible was melted at a temperature of typically about 50 °C above its melting point. The molten solder was then extruded vertically downward into air at room temperature through the outer nozzle of a coaxial nozzle mounted at the crucible bottom. Capillary instability of the extruded hollow molten solder jet led to the formation of hollow solder spheres. This formation was assisted by a transverse nozzle placed close to the coaxial nozzle, which directed an inert gas past the hollow jet at position where sphere detached. The spheres were then quickly cooled and solidified by water mist prior to collection in a container filled with water. Most of these spheres were completely hermetic and had a relatively smooth surface. Hollow water spheres were also formed as a test of production of hollow solder spheres through the nozzle.
収録刊行物
-
- JSMME
-
JSMME 4 (10), 1530-1538, 2010
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205263826304
-
- NII論文ID
- 130000420981
-
- ISSN
- 18809871
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可