Reaction sintering of polycrystalline cubic boron nitride at high pressure and temperature.
-
- Sumiya Hitoshi
- 住友電気工業(株)伊丹研究所
-
- Tsuji Kazuo
- 住友電気工業(株)伊丹研究所
-
- Yazu Shuji
- 住友電気工業(株)伊丹研究所
Bibliographic Information
- Other Title
-
- cBN多結晶体の超高圧高温反応焼結
- cBN タケッショウタイ ノ チョウコウアツ コウオン ハンノウ ショウケツ
Search this article
Abstract
Single phase sintered compact of cBN (polycrystalline cBN) may be prepared under high pressure and temperature (>5.2GPa, >1350°C) from hBN compact carrying a small amount of Mg3BN3 as a catalyst. This work investigated the influence of the amount of Mg3BN3 added to the hBN compact on the microstructure and the thermal conductivity of the prepared polycrystalline cBN. It was established that by controlling the amount of Mg3BN3 (-1.0mol%) it was possible to prepare polycrystalline cBN which had a high thermal conductivity, approximately 6W/cm°C at room temperature. In addition, it was found that a small amount of water diffused into the hBN compact containing Mg3BN3 would suppress abnormal growth of cBN particles. Thus, by adding 0.2wt% of water to the hBN compact containing 1.0mol% of Mg3BN3, a homogeneous cBN sintered compact having regular particles (5-8μm) and with high thermal conductivity (-7W/cm°C) could be consistently prepared.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 36 (6), 752-755, 1989
Japan Society of Powder and Powder Metallurgy
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001206308751744
-
- NII Article ID
- 130000813699
-
- NII Book ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 3248039
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed