- Chemical and Mechanical Stability of the High-Tc Phase in the Bi-Pb-Sr-Ca-Cu-O System. (I). Effects of Heat Treatment of Crushed Powder of the High-Tc Phase.
- Bi Pb Sr Ca Cu Oケイ コウオンソウ ノ カガクテキ オヨビ キ
- Effects of Heat Treatment of Crushed Powder of the High-Tc Phase
- 粉砕粉の熱処理効果
この論文をさがす
抄録
Chemical and mechanical stability of the high-Tc phase has been studied for the samples of Bi0.9Pb0.2Sr1.0Ca1.0Cu1.6Ox. Mechanical grinding converts the high-Tc phase into a nonsuperconducting amorphous phase. The ground high-Tc phase is not stabilized on annealing at lower temperatures below 820°C. Annealing at lower temperature leads to precipitation of some impurity phases and the low-Tc phase which depends on annealing temperature and time. The high-Tc phase is recovered by annealing at 850°C. The lattice parameters a and c of the high-Tc phase annealed at 850°C are longer than those below 820°C.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 39 (9), 779-782, 1992
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206305598208
-
- NII論文ID
- 130000818253
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3782633
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可