Ｂｉ‐２２２３相のピン止め力に及ぼすアニールの影響

• 草野 圭弘

  岡山大学工学部

• 大上 洋一

  岡山大学工学部

• 難波 徳郎

  岡山大学工学部

• 高田 潤

  岡山大学工学部

• 池田 靖訓

  京都大学化学研究所

• 高野 幹夫

  京都大学化学研究所

• 坂東 尚周

  京都大学化学研究所

書誌事項

タイトル別名

• Effect of Annealing on Pinning Force of Bi-2223 Phase.
• Bi 2223ソウ ノ ピンドメリョク ニ オヨボス アニール ノ エイキョウ

抄録

Pining characteristics due to the precipitates of the "3321"(Sr_2.5Bi_0.5Pb₃Ca₂CuO_z) phase have been studied in the Bi-2223 phase in the Bi-Pb-Sr-Ca-Cu-O system by mainly XRD and magnetic measurements. The precipitation of the "3321" phase was controlled by changing annealing temperature and annealing time in air. On annealing at 750°C for 10min and 1h, the larger hysteresis loops in M-H curves were observed in comparison with the initial one before annealing. However, the hysteresis loops became smaller with increasing precipitation of the "3321 " phase. Furthermore, the 2223 phase annealed at 400°C and 500°C, in which no precipitation of the "3321 " phase was observed, exhibits larger hysteresis loops.

収録刊行物

• 粉体および粉末冶金

  粉体および粉末冶金 41 (12), 1501-1504, 1994

  一般社団法人 粉体粉末冶金協会

キーワード

• Materials Chemistry
• Metals and Alloys
• Industrial and Manufacturing Engineering
• Mechanical Engineering

詳細情報

• CRID: 1390001206309251968
• NII論文ID: 130000819464
• NII書誌ID: AN00222724
• DOI: 10.2497/jjspm.41.1501
• ISSN: 18809014
• ISSN: 05328799
• NDL書誌ID: 3904266
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I3904266
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可