- Effect of Heating Atomosphere on Segregation and Dissolution of the Pb-compound in the Bi-2223 Phase.
- Bi 2223ソウ ニ オケル Pb カゴウブツ ノ セキシュツ サイ コヨウ
この論文をさがす
抄録
Thermal behavior of the Bi-2223 phase in the Bi, Pb-Sr-Ca-Cu-O system, especially segregation and dissolution reaction of the "3321" phase which was identified as Sr2.5Bi0.5Pb3Ca2CuO2, has been studied by XRD, SQUID and resistivity measurements. On annealing below 830°C in air, the "3321" phase precipitated from the 2223 crystals. When the 2223 phase was annealed at 750°C in O2stream, the precipitation of the "3321 " phase increased. On annealing at 750°C in Ar stream, however, no precipitation of the "3321" phase was detected. By reheateing at 850°C even for 1min, the "3321" phase was almost dissolved into the mother 2223 crystals. When the 2223 phase was reheated at 750°C in Ar stream after annealing at 750°C in air, the "3321 " phase disappeared. On the contrary, the "3321" phase was stable on reheating at 870°C in O2 stream. Therefore, it seems that the "3321" and the 2223 phase coexist in epuilibrium in a high oxygen partial pressure.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 41 (4), 388-391, 1994
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681285757952
-
- NII論文ID
- 130000819544
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3878302
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可