Method of Estimated Unloading Curve for Evaluation of Interfacial Strength by Nanoindentation Test
-
- KOZUKI Kentaro
- Tire Research Department, Bridgestone Corporation
-
- INABA Kazukaki
- 東京工業大学大学院理工学研究科
-
- KISHIMOTO Kikuo
- 東京工業大学大学院理工学研究科
Bibliographic Information
- Other Title
-
- ナノインデンテーション試験による界面強度評価のための推定除荷曲線法
Abstract
A new evaluation method was proposed for the interfacial strength between a thin film and its substrate by nanoindenation test. In this method, the released energy due to a coating delamination is obtained by estimating the shapes of the unloading curve at the points just after and before delamination on the load-displacement curve. Shape of unloading curves can be assumed by obtaining the contact stiffness of thin films. To confirm the validity of the method, nanoindentation tests were conducted for polyimide (PI) coating / Si substrate specimens and the interfacial strength was evaluated. Three specimens that have different thickness were prepared. Contact stiffness of PI film bears a linear relationship with indentation load. Irrespective of the coating thickness, the values of the interfacial strengths converge. In addition, the values of strengths agree with the results obtained by the authors in the previous paper for the case that small scale yielding conditions are satisfied. For the case that indentation loading rate is high and the delamination occurs before the relaxation of film, it is necessary to measure the contact stiffness with each indentation loading rate.
Journal
-
- TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
-
TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A 77 (776), 629-637, 2011
The Japan Society of Mechanical Engineers
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001204477021952
-
- NII Article ID
- 130000874041
-
- ISSN
- 18848338
- 03875008
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed