Synthetic inorganic ion-exchange materials. LVIII. Hydrothermal synthesis of a new layered lithium titanate and its alkali ion exchange.
-
- Sugita Mitsuru
- Department of Chemistry, Faculty of Science, Tokyo Institute of Technology
-
- Tsuji Masamichi
- Department of Chemistry, Faculty of Science, Tokyo Institute of Technology
-
- Abe Mitsuo
- Department of Chemistry, Faculty of Science, Tokyo Institute of Technology
抄録
A new crystalline hydrous lithium titanate, (Li1.81, H0.19)Ti2O5·2.2H2O, was synthesized hydrothermally at 190 °C by a reaction of hydrous titanium dioxide with LiOH solution. The compound has a layered structure and showed a C–base-centered orthorhombic system with the lattice constants, ao=16.66±0.02 Å, bo=3.797±0.002 Å, and co=3.007±0.003 Å. The lattice constants were changed to ao=18.08±0.03 Å, bo=3.784±0.003 Å, and co=2.998±0.002 Å upon conversion to the hydrogen form. The 8.5% increase in the ao value along the a axis suggests a layered structure. A hypothetical structure was proposed. The H+ form showed the ion-exchange selectivity at an ionic strength of 0.1 in the order of K+<Na+<Li+ at pH>6 and Li+<K+<Na+ at pH<6.
収録刊行物
-
- Bulletin of the Chemical Society of Japan
-
Bulletin of the Chemical Society of Japan 63 (7), 1978-1984, 1990
公益社団法人 日本化学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204117985792
-
- NII論文ID
- 130001979491
-
- ISSN
- 13480634
- 00092673
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可