Influence of La2O3 addition on thermophysical properties of ZrO2-4 mol %Y2O3 ceramics fabricated by spark plasma sintering
-
- JANG Byung-Koog
- High Temperature Materials Unit, National Institute for Materials Science
-
- KIM Seongwon
- Korea Institute of Ceramic Engineering and Technology
-
- OH Yoon-Suk
- Korea Institute of Ceramic Engineering and Technology
-
- KIM Hyung-Tae
- Korea Institute of Ceramic Engineering and Technology
-
- SAKKA Yoshio
- Materials Processing Unit, National Institute for Materials Science
-
- MURAKAMI Hideyuki
- High Temperature Materials Unit, National Institute for Materials Science
抄録
The influence of La2O3 addition on the thermal diffusivity and thermal conductivity of ZrO2 ceramics has been investigated. Porous and dense ZrO2 ceramics were fabricated by spark plasma sintering at 1100 and 1500°C. The porosity of ZrO2 ceramics sintered at 1100°C increased with increasing 0–5 mol % La2O3 addition. In contrast, ZrO2 ceramics sintered at 1500°C showed full density regardless of the amount of La2O3 addition. The La2Zr2O7 of crystalline pyrochlore phase was formed by reaction between La2O3 and ZrO2. The XRD peak of the La2Zr2O7 phase increased with increasing La2O3 addition. The thermal diffusivity and thermal conductivity of sintered ZrO2 decreased with increasing La2O3 addition. In addition, the thermal conductivity of the present samples decreased remarkably with increasing the porosity.
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 119 (1396), 929-932, 2011
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205287723264
-
- NII論文ID
- 130002067670
-
- ISSN
- 13486535
- 18820743
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可