- Improvement of Bending Strength and Fracture Toughness of C/C Composite by Adding Carbon Particles with 3-Dimensional Web-Like Structures
- リッタイ アミメ コウゾウ オ ユウスル タンソ フンマツ ノ テンカ ニ ヨル C/C フクゴウ ザイリョウ ノ マゲ キョウド オヨビ ハカイジンセイ ノ コウジョウ
この論文をさがす
抄録
This paper proposes an effective technique to improve bending strength and fracture toughness of C/C composite by adding carbonized Micro Fibrillated Cellulose (CMFC). In this study, conventional CFRP was carbonized at 1,700°C with inert atmosphere to fabricate the C/C composites in which char matrix was made from phenolic resin. In order to fabricate the carbon particles with 3-dimensional web-like structures, the absorbed water of market available MFC was eliminated by freeze-drying technique, then MFC was carbonized at 800°C with inert atmosphere. The improvement in the bending strength was appeared at the condition of 1.0wt% of addition, while the excessive addition of CMFC was not effective to improve the bending strength. The morphology evaluation of fracture surface was revealed that the fiber braking was observed at the condition of 1.0wt% of addition, while debonding was appeared on that of unmodified, 3.0 and 5.0wt% of CMFC addition. The interfacial shear strength and fracture toughness were also improved when matrix was modified with appropriate contents of CMFC. The effect of CMFC addition on bending strength and fracture toughness of carbon matrix was also investigated. The local fracture toughness evaluated by IF(Indentation Fracture) test was increased with increase of CMFC contents. However, the bending strength of carbon matrix was increased when 1.0wt% of CMFC addition, while the excessive addition of CMFC was not effective to improve the bending strength of carbon matrix. The agglomeration of CMFC was appeared due to the increment of viscosity of carbon precursor, when the excessive content of CMFC was added.
収録刊行物
-
- 材料
-
材料 61 (5), 468-473, 2012
公益社団法人 日本材料学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205443913472
-
- NII論文ID
- 130002084987
-
- NII書誌ID
- AN00096175
-
- COI
- 1:CAS:528:DC%2BC38XhtVShtrzP
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 023796800
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可