Preparation of novel potassium, lanthanum-iron oxides and their magnetic properties
-
- Yamamoto Tatsuhiro
- Graduate School of Science and Engineering, Saitama University
-
- Kamishima Kenji
- Graduate School of Science and Engineering, Saitama University
-
- Kakizaki Koichi
- Graduate School of Science and Engineering, Saitama University
-
- Hiratsuka Nobuyuki
- Graduate School of Science and Engineering, Saitama University
抄録
We have investigated the synthesis conditions, and the magnetic properties of M-type ferromagnetic potassium, lanthanum-iron oxides. The samples were prepared by solid-state-reaction. It is found that a new M-type ferrite can be effectively synthesized at 1275°C from the starting materials pulverized with a planetary ball mill. The magnetic transition temperature of the sample is 440°C which is quite close to that of the magnetoplumbite-type ferrite. EPMA compositional analysis for this new M-type ferrite shows the composition ratio of K : La : Fe = 0.75 : 0.90 : 18.58. From this result, the chemical formula of the magnetoplumbite phase in this sample is estimated to be K0.45La0.55Fe12O19-δ.
収録刊行物
-
- Transactions of the Materials Research Society of Japan
-
Transactions of the Materials Research Society of Japan 37 (2), 271-274, 2012
一般社団法人 日本MRS
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205512450560
-
- NII論文ID
- 130003399099
-
- COI
- 1:CAS:528:DC%2BC38Xht1aksL3J
-
- ISSN
- 21881650
- 13823469
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可