- Makino Noboru
- Faculty of Engineering, University of Tokyo, Tokyo, Japan, Tokyo Keiki Seizosho Co., Ltd.
-
- Suzuki Masaki
- Tokyo Keiki Seizosho Co., Ltd. (Tokyo Precision Equipiment Co., Ltd.)
抄録
Methods for preparing Mn-Bi and Mn-Al alloys and producing magnets from Mn-Bi alloys have been studied. A Mn-Bi alloy of high purity was prepared by sintering powders of Mn and Bi at 260°C for about 1000 hrs. Ferromagnetic Mn-Al alloys were prepared by quenching and tempering, and the influences of the temperatures of these treatments on the magnetic properties of the ferromagnetic Mn-Al alloy were studied in detail. To pulverize the Mn-Bi compound a hammer mill was used in an Argon atmosphere, and this gave good results. Mn-Bi magnets were produced by compressing power containing about 8% of resin at 200°C, and curing at 100°C. To obtain good magnetic properties, the magnetic field applied during compression should be 9,000 Oe or stronger. A magnet thus prepared has a Br of 2,500 to 3,800 gauss, and a BBC of 1,200 to 2,600 Oe. The thermal coefficient of remanence was about −1.23×10−3 gauss/°C.
収録刊行物
-
- Transactions of the Japan Institute of Metals
-
Transactions of the Japan Institute of Metals 2 (4), 228-232, 1961
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680095667968
-
- NII論文ID
- 130003485707
-
- ISSN
- 24324701
- 00214434
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可