High pressure synthesis of a new aluminium silicate: Al5Si5O17(OH).
-
- Eggleton R. A.
- Geology Department, Australian National University
-
- Boland J. N.
- Research School of Earth Sciences, Australian National University
-
- Ringwood A. E.
- Research School of Earth Sciences, Australian National University
Bibliographic Information
- Other Title
-
- High pressure synthesis of a new aluminum silicate: Al5Si5O17(OH)
Abstract
A new aluminium silicate has been produced under hydrous conditions from Al2O3-SiO2 oxide mixes with Si/Al ratios close to unity, at pressures greater than 100 kilobars and at about 1, 000°C. X-ray powder photographs indicated one dominant new phase. From analyses of the electron diffraction Laue zones of minute fragments (∼1μm), a monoclinic structure that fitted the X-ray powder results was identified. This monoclinic structure is described in terms of nine close-packed layers of oxygen with the unit cell containing 72 oxygen atoms. Assuming Si/Al equals 1, the composition of this phase is Al20Si20O72H4. The calculated density of 4.03 g/cc is in good agreement with the value of 4.02 g/cc estimated from the refractive index measurements.
Journal
-
- GEOCHEMICAL JOURNAL
-
GEOCHEMICAL JOURNAL 12 (3), 191-194, 1978
GEOCHEMICAL SOCIETY OF JAPAN
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282679526566400
-
- NII Article ID
- 130003743053
-
- ISSN
- 18805973
- 00167002
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed