電子ビーム溶接ビードの冷却過程と構造用鋼の硬化度の予測について
書誌事項
- タイトル別名
-
- On the Cooling Process and Prediction of Welds in Electron-Beam Welding
- Studies on Electron-Beam Welding (No. 9)
- 電子ビーム溶接に関する研究 9
抄録
The actual cooling rates in electron-beam welds for carbon steel, stainless steel, aluminium plates and zirconium sheet are compared with the theoretical cooling rates which are induced by the thermal conduction theory. According to this comparison, the actual cooling rates in the elec-tron-beam welds which show unique wedge-shape penetration agree with the theoretical cooling rates by the two-dimensional heat flow theory.<BR>Especially at the temperature below 900°C, the actual cooling rates and cooling curves in the electron-beam welds completely agree with those induced from the theoretical equation.<BR>With utilization of this theoretical equation, therefore, a nomograph from which is estimated the cooling time from 800°C to 500°C is made for a carbon steel of which the weld metal and heat affected zone are hardened when electron-beam welding is done. Moreover, the method for the estimation of hardness in the electron-beam welds is established with the use of the nomograph and C.C.T. diagram for welding and is discussed for the reliability. As a result of the discussion, it is seen that the above method for the estimation is reliable for carbon steel.
収録刊行物
-
- 溶接学会誌
-
溶接学会誌 33 (10), 918-927, 1964
一般社団法人 溶接学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206502507648
-
- NII論文ID
- 130003762913
-
- ISSN
- 18837204
- 00214787
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可