鋼溶接金属の窒素含量におよぼす合金元素の影響(第1報)
書誌事項
- タイトル別名
-
- Effect of Alloying Elements on Nitrogen Content of Steel Weld Metals (Report 1)
- Welding in Nitrogen Atmosphere
- 窒素雰囲気の場合
抄録
Using ten series of alloy steel electrode wires, mild steel was welded in a nitrogen atmosphere.<BR>The individual influence of the alloying elements, C, Si, Mn, Nb, Mo, V, Co, Ta, W and Cu in the electrode wires on the nitrogen content of weld metals was systematically studied.<BR>The results are summarized as follows;<BR>1) The nitrogen content of weld metals increases with increasing the vanadium, niobium, tungsten, molybdenum, tantalum and manganese contents in electrode wires.<BR>2) The nitrogen content of weld metals decreases with increasing the carbon and silicon contents in electrode wires.<BR>3) Cobalt and copper have no significant influence.<BR>4) The effects of alloying elements in electrode wires on the nitrogen content of weld metals are generally similar to their effects on the solubility of nitrogen in liquid iron alloys.<BR>5) The influence of each alloying element on the nitrogen absorption by weld metals during are welding was estimated by analogy with thermodynamics.
収録刊行物
-
- 溶接学会誌
-
溶接学会誌 41 (3), 308-321, 1972
一般社団法人 溶接学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681477912192
-
- NII論文ID
- 130003763209
-
- ISSN
- 18837204
- 00214787
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可