Study on the Type of Friction Welding (Report 2)
-
- Hira Hirohito
- Kawasaki Heavy Industries Ltd.
-
- Kanatani Fumiyoshi
- Kawasaki Heavy Industries Ltd.
-
- Uemura Takao
- Kawasaki Heavy Industries Ltd.
-
- Shiomi Atsushi
- Kawasaki Heavy Industries Ltd.
-
- Amano Kazuo
- Kawasaki Heavy Industries Ltd.
Bibliographic Information
- Other Title
-
- 摩擦圧接方式に関する研究 II 板と丸棒との摩擦圧接について
- 板と丸棒との摩擦圧接について
Abstract
In the previous report, difference between brake type and inertia type friction welding was discussed, then effect of various parameters on burn-off behaviours and macrostructures of the same diameter bar friction welds was studied. Deceleration condition of rotation was shown very effective parameter.<BR>In this report, friction welding parameters and joint design for the welding of stud to plate joint was considered.<BR>Experimental results were as follows;<BR>1) Friction welding of stud to plate joint was relatively difficult than welding of same diameter bar joint, because some characteristic defects caused by the shape effect was appeared. So, the parameters of higher pressure and longer deceleration time should be used for the stud to plate joint than those for same diameter bar joint.<BR>2) When same welding condition was used for both stud to plate and same diameter bar joint, the former showed rather convex shape heat affected zone.<BR>3) Heat affected zone of stud to plate joint became narrower and concave shape with increase of pres-sure and deceleration time similarly the case of same diameter bar joint.<BR>4) Movement of friction surface from the plate face to stud was occurred when low pressure was used for stud to plate joint. And moved zone was difficult to be removed only by using high upsetting pressure.<BR>5) Protrusion should be prepared when frictoin pressure was restricted to the low level.
Journal
-
- JOURNAL OF THE JAPAN WELDING SOCIETY
-
JOURNAL OF THE JAPAN WELDING SOCIETY 51 (8), 693-700, 1982
JAPAN WELDING SOCIETY
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001206499037952
-
- NII Article ID
- 130003763650
-
- ISSN
- 18837204
- 00214787
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed