高張力鋼溶接熱影響部における再熱割れの研究
書誌事項
- タイトル別名
-
- A Study of Reheat Cracking in Weld Heat-Affected Zone of High Strength Steel
抄録
A mechanism and some factors to cause a reheat cracking in HAZ of high strength steel weldment were examined and discussed, using a T-1 type of steel.<BR>The following results were obtained in this study.<BR>(1) The reheat cracking in HAZ can be induced by both a segregation of impurities and a precipitation of carbides of secondary hardening elements at grain boundaries. In particular, the effect of a grain boundary precipitation is predominant in case of T-1 type of steel HAZ.<BR>(2) It is likely that the influence of carbides precipitated at grain boundaries on the reheat cracking susceptibility appears through a decohesion at grain boundary and a lowering of a deformability or a ductility at grain boundary because of an intense interaction between dislocations and carbides.<BR>(3) The effects of a segregation of impurities and a precipitation of carbides at grain boundary on the reheat cracking phenomenon were able to be represented schematically.
収録刊行物
-
- 溶接学会論文集
-
溶接学会論文集 1 (1), 37-44, 1983
一般社団法人 溶接学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204722763520
-
- NII論文ID
- 130003764348
-
- ISSN
- 24348252
- 02884771
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可