き裂を含む異種材接合部の強度評価  [in Japanese] Evaluation of Bonding Strength of Dissimilar Material Joints with an Interface Crack.  [in Japanese]

Access this Article

Author(s)

Abstract

In this study, critical J-value was used as the parameter of bonding strength criterion of dissimilar material joints with an interface crack. J-value was calculated by finite element method. The effect of several factors (Young's Modulus ratio, Difference in coefficient of thermal expansion, Temperature variations, Crack length etc.) on J-value was discussed. Fracture tests were carried out using specimens that were bonded using an insert material. Critical J-value was analyzed from both breaking load of fracture test and thermal stress induced by temperature variations from bonding temperature to test temperature. This value was not affected by initial crack length and insert material thickness. Therefore, this value was reasonable as parameter of bonding strength criterion of joints. From the results, it was found that this method was valid as the evaluation method of bonding strength of dissimilar material joints.

Journal

  • QUARTERLY JOURNAL OF THE JAPAN WELDING SOCIETY

    QUARTERLY JOURNAL OF THE JAPAN WELDING SOCIETY 12(3), 445-450, 1994

    JAPAN WELDING SOCIETY

Codes

  • NII Article ID (NAID)
    130003764440
  • Text Lang
    JPN
  • ISSN
    0288-4771
  • Data Source
    J-STAGE 
Page Top