フェライト単相で凝固するオーステナイト系ステンレス鋼溶接金属におけるアシキュラー状組織の形成に及ぼすマッシブ変態の影響 Cr‐Ni系ステンレス鋼溶接金属の凝固・変態に関する研究 (第5報)

DOI

書誌事項

タイトル別名
  • Effect of Massive Transformation on Formation of Acicular Structure in Austenitic Stainless Steel Weld Metal Solidified as Ferritic Single Phase. Study on Solidification and Subsequent Transformation of Cr-Ni Stainless Steel Weld Metals. (Report 5).
  • Study on Solidification and Subsequent Transformation of Cr-Ni Stainless Steel Weld Metals (Report 5)
  • Cr-Ni系ステンレス鋼溶接金属の凝固・変態に関する研究(第5報)

抄録

In austenitic stainless steel weld metals solidified as ferritic single phase, subsequent ferrite-to-austenite transformation could be massive when the postsolidification cooling is rapid as in GTA welding. On the other hand, this GTA weld metal shows acicular structure of ferrite and austenite at room temperature microstructure. The effect of massive transformation on the formation of acicular structure was investigated in this study using different thermal cycle patterns and quenching technique. Massive transformation occurs below the T0 temperature within the two-phase region of ferrite and austenite at a cooling rate of approximately 100K/sec. On cooling after the massive transformation, austenite continues to grow into retained ferrite epitaxially from massive austenite while ferrite precipitates again at twin boundaries within the massive austenite. This suggests that acicular structure of ferrite and austenite is formed even if the massive transformation occur. In this case, the grain refinement and rapid progress of structure formation are expected as compared with weld metals in which massive transformation does not occur.

収録刊行物

詳細情報

  • CRID
    1390001204722973696
  • NII論文ID
    130003764566
  • DOI
    10.2207/qjjws.15.305
  • ISSN
    24348252
    02884771
  • 本文言語コード
    ja
  • データソース種別
    • JaLC
    • Crossref
    • CiNii Articles
  • 抄録ライセンスフラグ
    使用不可

問題の指摘

ページトップへ