Ｔｉ‐Ｃｕ‐Ｃｒろうによるチタンのろう付

• 雀部 謙

  金属材料技術研究所

• 平野 和夫

  萬世工業株式会社

書誌事項

タイトル別名

• Brazing of titanium with Ti-Cu-Cr filler alloy.

抄録

Mechanical properties of work hardened pure titanium joint brazed with Ti-Cu-Cr-Al filler metal were investigated.<BR>Test specimens were brazed with filler metal containing 29%Ti, 62.5%Cu, 6.5%Cr and 2%Al in a vacuum. Brazing temperature were 850°C, 900°C, 1, 000°C and 1, 100°C for 10sec. Tensile strength of butt joints were comparable to that of joints brazed with conventional Ti-Ni-Cu filler metal, and hardness at the joint was lower. The reaction of filler metal with base metal was modertely and damage of base metals were less. The addition of pressure to joint during brazing gave significant effect on joint strength.

収録刊行物

• 溶接学会論文集

  溶接学会論文集 8 (3), 354-359, 1990

  一般社団法人 溶接学会

キーワード

• Brazing
• Titanium
• Ti-Cu-Cr filler metal
• Butt joint
• Rapid brazing
• Tensile strength
• Hardness at joint
• Pressure during brazing

詳細情報

• CRID: 1390282679700039936
• NII論文ID: 130003764910
• DOI: 10.2207/qjjws.8.354
• ISSN: 24348252
• ISSN: 02884771
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可