Ultrasonic Behavior of Liquid Tin-Bismuth Alloys above Melting Point
-
- Kamioka Hiroaki
- Department of Physics, Faculty of Engineering, Gifu University
-
- Sumino Yoshio
- Regional Center for Earthquake Prediction and Observation, Faculty of Science, Nagoya University
書誌事項
- タイトル別名
-
- Ultrasonic Behavior of Liquid Tin Bismu
この論文をさがす
抄録
The sound velocity and its attenuation of three kinds of liquid tin-bismuth alloys, one eutectic composition of Bi/(Bi+Sn)=57.0 wt% and two hyper-eutectic compositions of Bi/(Bi+Sn)=63.5 and 66.7 wt%, were measured by the pulse transmission method over a range of temperatures extending from 139°C (eutectic temperature) to 190°C. The sound velocity of each liquid alloy shows the steady decrease with temperature in the measured temperature range, and the temperature coefficients of sound velocity in Bi57.0Sn43.0, Bi63.5Sn36.5 and Bi66.7Sn33.3, were −0.002, −0.589 and −0.660 m/s·deg at 170°C, respectively. By combining the present results with the previous data of density and thermal expansivity, the elastic and anelastic properties of liquid tin-bismuth alloys were reported, and discussion was made on the obtained results.
収録刊行物
-
- Journal of the Physical Society of Japan
-
Journal of the Physical Society of Japan 53 (9), 3036-3041, 1984
一般社団法人 日本物理学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679161664640
-
- NII論文ID
- 110001966982
- 130003898299
- 210000091582
-
- NII書誌ID
- AA00704814
-
- BIBCODE
- 1984JPSJ...53.3036K
-
- COI
- 1:CAS:528:DyaL2cXlslOqsbk%3D
-
- ISSN
- 13474073
- 00319015
-
- NDL書誌ID
- 2991892
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可