鋼線の疲労に関する研究(第3報)

• 上田 太郎

  大阪大学工学部

• 朝倉 健二

  大阪大学工学部

書誌事項

タイトル別名

• Investigation on the Fatigue Properties of Steel Wire (Part 3)
• Behavior of the Longitudinal Residual Stress of Cold Drawn Steel Wire Subjected to the Repeated Stress
• 繰返応力による硬鋼線の軸方向残留応力の挙動について

抄録

This investigation was planned for researching the effect of the repeated stress upon the longitudinal residual stress existing in the cold drawn carbon steel wire. For the specimen, 0.65% carbon steel wires drawn with 60% and 80% reductions were used, and the diameter of these wires was 1.3mm.<BR>For the measurement of the longitudinal residual stresses existing in these fine steel wires, the present writers adopted the mechanical method and electro-magnetic method.<BR>Hunter fatigue testing machine was used in this investigation, and from S-N curves of these wires the fatigue limit stress and three stresses over the fatigue limit were chosen as the repeated stress to research the behavior of residual stress. The fatigue test specimens were taken out from the fatigue testing machine at 10⁷ and 10⁶ cycles for the fatigue limit stress and at the number of cycle just before the break down cycle for each stress over the fatigue limit, and then the specimens for measurement of residual stress were cut out from the middle part of these fatigue test specimens. The distributions of longitudinal residual stresses of these specimens subjected to the repeated stresses were measured and those were compared with that of the standard specimen not subjected to the repeated stress.<BR>From the results obtained by this investigation, it was made clear that if the longitudinal tensile residual stress existing in the outer part of the wire was about 20-30kg/mm², the distribution of longitudinal residual stress of the cold drawn steel wire was little affected by the repeated stress under rotating bending over the fatigue limit, and that which is equal to the fatigue limit, either.

収録刊行物

• 材料試験

  材料試験 9 (78), 192-199, 1960

  公益社団法人 日本材料学会

詳細情報

• CRID: 1390001205393249024
• NII論文ID: 130003929477
• DOI: 10.2472/jsms1952.9.192
• ISSN: 03727971
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可