鉄筋の腐食膨張によるひびわれの発生機構に関する基礎的研究

• 森川 雅行

  社団法人 土木学会 運輸省前第二港湾建設局 横浜調査設計事務所

• 関 博

  社団法人 土木学会 早稲田大学 理工学部土木工学科

• 奥村 隆

  社団法人 土木学会 清水建設株式会社 (土木本部)

書誌事項

タイトル別名

• BASIC STUDY ON CRACKING OF CONCRETE DUE TO EXPANSION BY REBAR CORROSION
• テッキン ノ フショク ボウチョウ ニ ヨル ヒビワレ ノ ハッセイ キコウ

抄録

To investigate the mechanism of concrete cracking by rebar corrosion, an accelerated test by electrolytic corrosion has been done. Additional chemical analysises were also carried out to confirm corrosion characteristics. During acceleration, free chlorides moved toward the anode and corrosion products did not move away from the steel-mortar interface. X-ray diffraction results indicated that corrosion products consisted mainly of Fe₃O₄. Not only resistance of concrete against internal pressure but also corrosion rate had influence on weight-loss of steel for cracking. When the corrosion rate was more than 0.5mpy, 3-9mg/cm² of weight-loss was enough for cracking and an elastic analysis was effective for its presumption.

収録刊行物

• 土木学会論文集

  土木学会論文集 1987 (378), 97-105, 1987-02-20

  公益社団法人 土木学会

キーワード

• expansive cracking
• chloride
• corrosion of bar
• corrosion products

詳細情報

• CRID: 1390001205600976512
• NII論文ID: 130003980631
• NII書誌ID: AN10014020
• DOI: 10.2208/jscej.1987.378_97
• ISSN: 18827187
• ISSN: 02897806
• ISSN: http://id.crossref.org/issn/02897806
• NDL書誌ID: 3115609
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I3115609
• Web Site: https://www.jstage.jst.go.jp/article/jscej1984/1987/378/1987_378_97/_pdf
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可