- Glassy Carbon from Sulfonated Polystyrenet
抄録
For the purpose of preparing glassy carbon from thermoplastic resins, spherical particles of polystyrene were made infusible by the sulfonation and pyrolyzed at 200-1600°C. The following three methods were performed for sulfonation; (a) sulfonation of polystyrene particles with SO3 gas, (b) sulfonation of the polystyrene solution in C2H4Cl2 with the mixture of fuming sulfuric acid and C2H4Cl2 (1:1), and (c) direct sulfonation of polystyrene particles with fuming sulfuric acid. The last method was most effective to obtain infusible cross-linked polymer as shown in Table 1. Spherical hard carbon particles of 100-150μ diameter were obtained by pyrolyzing the sulfonated polystyrene at high temperatures. Carbonization process were pursued by micrograph, the measurement of weight loss, elemental analysis, and so on (Figs.1-3). X-ray diffraction patterns of carbon formed were very analogous to those of a phenolic resin carbon, and the crystal parameters, d002, Lc, and La showed the characteristic values for non-graphitizable carbon. The stability against air oxidation measured by differential thermal analysis was comparable to that of glassy carbon (Fig.4). BET surface area, density, and micro-Vicker's hardness were also measured as a function of heat treatment temperature (Figs.5-7), and were compared with the results for glassy carbon. As the results, the carbonaceous products from sulfonated polystyrene were found to be non-graphitizable hard carbon with the functions equivalent to usual glassy carbon from thermosetting resins.
収録刊行物
-
- 日本化学会誌(化学と工業化学)
-
日本化学会誌(化学と工業化学) 1979 (3), 403-407, 1979
公益社団法人 日本化学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679395387520
-
- NII論文ID
- 130004156401
-
- ISSN
- 21850925
- 03694577
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可