Ａｌ‐７％Ｓｉ‐０．３％Ｍｇ合金の熱処理について

• 佃 誠

  (株)神戸製鋼所

• 小池 進

  (株)神戸製鋼所

• 原田 雅行

  (株)神戸製鋼所

書誌事項

タイトル別名

• The heat treatment of Al-7%Si-0.3%Mg alloy
• Al 7パーセント Si 0 3パーセント Mg ゴウキン ノ ネツ ショリ

抄録

T6 conditions were examined on the Al-6.85%Si-0.30%Mg-0.20%Fe-0.12%Ti-1.006%Na alloy castings to select an optimum heat treating condition for automobile wheels. Solution heat treating at 540°C for 9hr and quenching into cold water (15°C) as soon as possible are recommended. The elongation and Charpy impact value are reduced by quenching in hot water or quenching after prolonged delay time. Aging at 180°C for 6hr ensures the highest strength, and aging at 140°C for 4hr does high elongation and impact strength.

収録刊行物

• 軽金属

  軽金属 28 (1), 8-14, 1978

  一般社団法人 軽金属学会

キーワード

• Materials Chemistry
• Metals and Alloys
• Mechanical Engineering
• Mechanics of Materials

詳細情報

• CRID: 1390282681315654656
• NII論文ID: 130004207956
• NII論文ID: 10004011171
• NII書誌ID: AN00069773
• DOI: 10.2464/jilm.28.8
• COI: 1:CAS:528:DyaE1MXitVygtLg%3D
• ISSN: 18808018
• ISSN: 04515994
• NDL書誌ID: 1923679
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I1923679
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可