- θ' structure in relation to nucleation sites for θ' phase in Al-Cu alloys
- Al Cu ゴウキン ニ オケル シータ ソシキ ト ソノ カク セイセイ サ
この論文をさがす
抄録
Transmission electron microscopy was carried out on the Al-4%Cu alloy solution-treated at 793K for 7.2ks, quenched into iced water or directly quenched to an aging bath and subsequently aged for different times. Homogeneous precipitation of a θ' phase never occurs in any cases. The θ' structure actually observed is controlled by the θ' precipitates formed on dislocation loops, dislocation lines and/or θ". The θ' precipitates form on dislocation loops if specimens were water quenched or direct-quenched to comparatively low temperatures and aged; on considerably sparse dislocation lines if direct-quenched where neither loops nor θ" appear; and form on θ" if direct-quenched where loops never appear but θ" precipitates develope.
収録刊行物
-
- 軽金属
-
軽金属 32 (1), 26-31, 1982
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206336181376
-
- NII論文ID
- 130004208256
- 10004549296
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DyaL3sXhtlSltro%3D
-
- ISSN
- 18808018
- 04515994
- http://id.crossref.org/issn/04515994
-
- NDL書誌ID
- 2435743
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可