- Improvement of bending strength in aluminum alloy matrix composites containing short alumina fibers by centrifugal force.
- エンシンリョク ニ ヨル アルミナ タンセンイ キョウカ アルミニウム ゴウキ
この論文をさがす
抄録
Cylindrical aluminum alloy matrix composites (MMC) containing alumina fibers were fabricated by applying a centrifugal force to fibrous preforms at room temperature before infiltration. Fiber segregation towards the outer periphery disappeared after infiltration, since boiling of carbon-tetrachloride as a mixture with the fibers relieved fiber segregation at the drying stage between the centrifuge and infiltration processes. However, the fibers tended to be aligned with a tangential direction of cylindrial fibrous preform by a centrifugal force. The MMC with high fiber volume fraction (Vf) showed only a poor alignment of fiber due to the dense fiber packing, while the one with low-Vf also showed a poor alignment due to long fiber length. Consequently, the MMC with Vf of nearly 20% showed the highest strengthening efficiency in bending tests. The bending strength increased with increasing Vf, and showed about a 200MPa rise compared to those of the MMC with the planar-randomly oriented fibers and the same Vf.
収録刊行物
-
- 軽金属
-
軽金属 40 (1), 7-12, 1990
一般社団法人 軽金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681311730944
-
- NII論文ID
- 130004208938
- 10002978643
-
- NII書誌ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
- http://id.crossref.org/issn/04515994
-
- NDL書誌ID
- 3655498
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可