- Microstructural change during superplastic deformation of the Mg-8 mass % Li alloy.
- Mg 8パーセント Li ゴウキン ノ チョウソセイ ヘンケイチュウ ノ ソシ
この論文をさがす
抄録
Microstructural changes during superplastic deformation at 573K have been investigated of a Mg-8 mass%Li eutectic alloy under both cast and thermomechanically processed conditions. The elongation of about 300% is obtained for ascast specimen under the superplastic condition, which is increased by finer grain-structure developed by more rapid solidification. Needle like α phase is observed to change to an equiaxed shape during superplastic deformation, and the mvalue of 0.2 at the initial period correspondingly increases during the deformation. ln the specimen of the recrystallized structure, twinning is observed in the α phase at the initial stage of superplastic deformation. The α grains are found to grow during the deformation, while the refining of β grains takes place. As a result, the mean grain size is slightly increased during deformation. These microstructural changes will play an important role to exhibit superplasticity.
収録刊行物
-
- 軽金属
-
軽金属 42 (3), 125-131, 1992
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681314914432
-
- NII論文ID
- 130004209208
- 10003135892
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DyaK38XitF2nsr0%3D
-
- ISSN
- 18808018
- 04515994
- http://id.crossref.org/issn/04515994
-
- NDL書誌ID
- 3759845
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可