高周波焼入れ粉末焼結歯車の疲れ強さに及ぼす粉末粒子径の影響

• 吉田 彰

• 大上 祐司

• 川崎 裕章

• 烏野 勇

書誌事項

タイトル別名

• Influence of Particle Diameter of Steel Powder on Fatigue Strength of Induction-Hardened Sintered Powder Metal Gears.
• コウシュウハ ヤキイレ フンマツ ショウケツ ハグルマ ノ ツカレ ツヨサ ニ

抄録

In order to elucidate the influences of particle size of steel powder on the surface durability of induction-hardened sintered powder metal gears, the gears with three kinds of particle sizes were fatigue-tested using a power circulating gear testing machine. The three kinds of particle diameters were under 45μm, 75μm∼106μm and 150μm∼250μm, respectively. The surface durability of the gear with the smallest particle size was almost equal to that of the gear with the intermediate particle size. While the surface durability of the gear with the largest particle size was inferior to those of the other gears. The smaller the particle size became, the smaller the pore size became and the lager the pore cluster factor by fractal dimension became. The failure mode of all gears was spalling with pitting. It was understood that the pore size and the pore cluster factor were important parameters to evaluate the surface durability of the sintered powder metal gears.

収録刊行物

• 日本機械学会論文集Ｃ編

  日本機械学会論文集Ｃ編 64 (622), 2191-2198, 1998

  一般社団法人 日本機械学会

キーワード

• Gear
• Induction-Hardened Sintered Powder Metal Gear
• Surface Durability
• Particle Diameter
• Pitting
• Spalling
• Pore

詳細情報

• CRID: 1390001206328233216
• NII論文ID: 130004232787
• NII論文ID: 110002383810
• NII書誌ID: AN00187463
• DOI: 10.1299/kikaic.64.2191
• COI: 1:CAS:528:DyaK1cXltlKgtr0%3D
• ISSN: 18848354
• ISSN: 03875024
• NDL書誌ID: 4504350
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I4504350
• Web Site: http://www.jstage.jst.go.jp/article/kikaic1979/64/622/64_622_2191/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可