セグメント化ポリウレタン‐ウレア弾性繊維の構造と物性　第２報　　応力‐歪み曲線のヒステリシス

DOI Web Site 被引用文献2件 参考文献13件

書誌事項

タイトル別名
  • Structure and Properties of Segmented Poly(urethane-urea) Elastic Fibers. Part 2: Hysteresis of Stress-Strain Curves.
  • セグメントカ ポリウレタン ウレア ダンセイ センイ ノ コウゾウ ト ブッセイ ダイ2ホウ オウリョク ヒズミ キョクセン ノ ヒステリシス
  • Part2 : Hysteresis of Stress-Strain Curves
  • 第2報 : 応力―歪み曲線のヒステリシス

この論文をさがす

抄録

The effects of pre-elongation ratio, stress relaxation time and recovery time on the hysteresis behavior of the stress-strain curve are discussed for segmented poly (urethane-urea).<BR>The loss of stress and extension energy was found to be much larger than unrecovered strain with pre-elongation. In the range of low extension ratio of α<2, the large loss in shear modulus was shown for unloading and re-elongation curves. However the breaking energy of the linkages was lower than 0.75 kJ/mol. As for the range of 2<α<3.5, the linkages having the bond energy of 20kJ/mol were broken by pre-elongation. The pre-elongation of α>4 led to break the linkages having the strong bond energy of 75kJ/mol. This energy corresponds to the break down of intermolecular hydrogen bond of hard segment. The molecular weight between crosslink points (Mc) estimated by shear modulus of unloading or re-elongation curves was almost the same as that of the prepolymer. The strong hydrogen bond of 75kJ/mol between hard segments re-bonded and recovered faster than other weaker linkages.<BR>The Mooney-Rivlin plots of unloading and re-elongation curves had much smaller values of C2 than those of the pre-elongation curves. This suggests that the strain softening effect decreased by pre-elongation. It is especially interesting that the unloading curve for elongation of α>4 had the value of C2_??_0 and showed ideal rubber elasticity.

収録刊行物

  • 繊維機械学会誌

    繊維機械学会誌 54 (3), T43-T49, 2001

    一般社団法人 日本繊維機械学会

被引用文献 (2)*注記

もっと見る

参考文献 (13)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ